Review article
A review of enhanced hydrogen storage in MgH2: the role of high-energy reactive ball milling and catalysis
- 1 Center for Nanoscience and Nanotechnology, Institute for Convergence Science & Technology, Sharif University of Technology, Tehran 14588-89694, Iran
- 2 Faculty of Materials and Manufacturing Technologies, Malek Ashtar University of Technology, Tehran, Iran
Abstract
Due to its significant hydrogen capacity (7.6 wt%), availability, and reversibility, magnesium hydride (MgH2) is considered one of the most promising solid-state hydrogen storage materials, making it attractive for sustainable energy systems. The excellent thermodynamic stability and slow absorption/desorption kinetics, which require elevated operating temperatures, limit its practical application. This paper addresses the important issue of how advanced synthesis methods, specifically high-energy reactive ball milling and catalytic doping, can overcome inherent challenges and enable the practical use of MgH2 for hydrogen storage. The methodology adopted is a systematic and integrative review of state-of-the-art experimental and theoretical studies, focusing on thermodynamic and kinetic fundamentals, synthesis routes, catalytic additives, and nanostructuring strategies. Results indicate that high-energy ball milling significantly improves hydrogen diffusion by reducing particle sizes to the nanoscale and lowering the desorption onset temperature by approximately 45 °C. Catalysts such as 2 mol% Nb2O5 further reduce activation energy barriers, enabling rapid hydrogen release of 6.4 wt% in 114 s, while polymorphic transitions (γ-MgH2 formation) enhance structural stability. Despite these advances, challenges such as grain coarsening and cycling capacity loss remain, highlighting the importance of nanoencapsulation, alloying, and scalable fabrication techniques. In conclusion, the review provides a critical framework for understanding the synergistic role of ball milling and catalysis in tailoring MgH2 properties and outlines future research directions toward efficient, scalable, and application-ready hydrogen storage systems.
Downloads
Download data is not yet available.
Keywords:
MgH2, Hydrogen storage, Thermodynamics, High-energy reactive ball milling, Catalysis
References
[1] I.P. Jain, C. Lal, A. Jain, Hydrogen storage in Mg: a most promising material, Int. J. Hydrog. Energy. 35 (2010) 5133–5144. https://doi.org/10.1016/j.ijhydene.2009.08.088.
[2] M. Paskevicius, D.A. Sheppard, C.E. Buckley, Thermodynamic changes in mechanochemically synthesized magnesium hydride nanoparticles, J. Am. Chem. Soc. 132 (2010) 5077–5083. https://doi.org/10.1021/ja908398u.
[3] J.F. Stampfer Jr, C. Holley Jr, J. Suttle, The magnesium-hydrogen system1-3, J. Am. Chem. Soc. 82 (1960) 3504–3508. https://doi.org/10.1021/ja01499a006.
[4] Z.-K. Qin, L.-Q. He, X.-L. Ding, T.-Z. Si, P. Cui, H.-W. Li, Y.-T. Li, Liquid Channels Built-In Solid Magnesium Hydrides for Boosting Hydrogen Sorption, Inorganics. 11 (2023) 216. https://doi.org/10.3390/inorganics11050216.
[5] C. Zhou, J. Zhang, R.C. Bowman, Z.Z. Fang, Roles of Ti-Based Catalysts on Magnesium Hydride and Its Hydrogen Storage Properties, Inorganics. 9 (2021) 36. https://doi.org/10.3390/inorganics9050036.
[6] L. Ren, Y. Li, N. Zhang, Z. Li, X. Lin, W. Zhu, C. Lu, W. Ding, J. Zou, Nanostructuring of Mg-Based Hydrogen Storage Materials: Recent Advances for Promoting Key Applications, Nano-micro Lett. 15 (2023) 93. https://doi.org/10.1007/s40820-023-01041-5.
[7] M. Lutz, M. Linder, I. Bürger, High capacity, low pressure hydrogen storage based on magnesium hydride and thermochemical heat storage: Experimental proof of concept, Appl. Energy. 271 (2020) 115226. https://doi.org/10.1016/j.apenergy.2020.115226.
[8] J.C. Crivello, B. Dam, R.V. Denys, M. Dornheim, D.M. Grant, et al., Review of magnesium hydride-based materials: development and optimisation, Appl. Phys. A. 122 (2016) 97. https://doi.org/10.1007/s00339-016-9602-0.
[9] J. Huot, D.B. Ravnsbæk, J. Zhang, F. Cuevas, M. Latroche, T.R. Jensen, Mechanochemical synthesis of hydrogen storage materials, Prog. Mater. Sci. 58 (2013) 30–75. https://doi.org/10.1016/j.pmatsci.2012.07.001.
[10] P. Vajeeston, P. Ravindran, B. Hauback, H. Fjellvåg, A. Kjekshus, et al., Structural stability and pressure-induced phase transitions in MgH2, Phys. Rev. B - Condens. Matter Mater. Phys. 73 (2006) 224102. https://doi.org/10.1103/PhysRevB.73.224102.
[11] P. Marty, P. de Rango, B. Delhomme, S. Garrier, Various tools for optimizing large scale magnesium hydride storage, J. Alloys Compd. 580 (2013) S324-S328. https://doi.org/10.1016/j.jallcom.2013.02.169.
[12] W. Zachariasen, C. Holley, J. Stamper, Neutron diffraction study of magnesium deuteride, Acta Crystal. 16 (1963) 352–353. https://doi.org/10.1107/S0365110X63000967.
[13] M. Bortz, B. Bertheville, G. Böttger, K. Yvon, Structure of the high pressure phase γ-MgH2 by neutron powder diffraction, J. Alloys Compd. 287 (1999) L4–L6. https://doi.org/10.1016/S0925-8388(99)00028-6.
[14] J. Zheng, L. Chen, J. Wang, X. Xi, H. Zhu, Y. Zhou, J. Wang, Thermodynamic analysis and comparison of four insulation schemes for liquid hydrogen storage tank, Energy Convers. Manage. 186 (2019) 526–534. https://doi.org/10.1016/j.enconman.2019.02.073.
[15] Z. Chen, K.O. Kirlikovali, K.B. Idrees, M.C. Wasson, O.K. Farha, Porous materials for hydrogen storage, Chem. 8 (2022) 693–716. https://doi.org/10.1016/j.chempr.2022.01.012.
[16] L. Ouyang, K. Chen, J. Jiang, X.-S. Yang, M. Zhu, Hydrogen storage in light-metal based systems: A review, J. Alloys Compd. 829 (2020) 154597. https://doi.org/10.1016/j.jallcom.2020.154597.
[17] B. Sakintuna, F. Lamari-Darkrim, M. Hirscher, Metal hydride materials for solid hydrogen storage: a review, Int. J. Hydrog. Energy. 32 (2007) 1121–1140. https://doi.org/10.1016/j.ijhydene.2006.11.022.
[18] J.J. Reilly Jr, R.H. Wiswall Jr, Reaction of hydrogen with alloys of magnesium and nickel and the formation of Mg2NiH4, Inorg. Chem. 7 (1968) 2254–2256. https://doi.org/10.1021/ic50069a016.
[19] S. Halilov, D. Singh, M. Gupta, R. Gupta, Stability and electronic structure of the complex K 2 Pt Cl 6-structure hydrides DMH 6 (D= Mg, Ca, Sr; M= Fe, Ru, Os), Phys. Rev. B - Condens. Matter Mater. Phys. 70 (2004) 195117. https://doi.org/10.1103/PhysRevB.70.195117.
[20] X. Huang, X. Xiao, Y. He, Z. Yao, X. Ye, H. Kou, C. Chen, T. Huang, X. Fan, L. Chen, Probing an intermediate state by X-ray absorption near-edge structure in nickel-doped 2LiBH4–MgH2 reactive hydride composite at moderate temperature, Mater. Today Nano. 12 (2020) 100090. https://doi.org/10.1016/j.mtnano.2020.100090.
[21] V.N. Kudiyarov, R.R. Elman, N.E. Kurdyumov, The Effect of High-Energy Ball Milling Conditions on Microstructure and Hydrogen Desorption Properties of Magnesium Hydride and Single-Walled Carbon Nanotubes, Metals. 11 (2021) 1409. https://doi.org/10.3390/met11091409.
[22] D.S. Korablov, O.V. Bezdorozhev, S. Gierlotka, V.A. Yartys, Y.M. Solonin, Effect of Various Additives on the Hydrolysis Performance of Nanostructured MgH2 Synthesized by High-Energy Ball Milling in Hydrogen, Powder Metall. Met. Ceram. 59 (2021) 483–490. https://doi.org/10.1007/s11106-021-00193-6.
[23] G. Liang, J. Huot, S. Boily, A. Van Neste, R. Schulz, Hydrogen storage properties of the mechanically milled MgH2–V nanocomposite, J. Alloys Compd. 291 (1999) 295–299. https://doi.org/10.1016/S0925-8388(99)00268-6.
[24] F. Cuevas, D. Korablov, M. Latroche, Synthesis, structural and hydrogenation properties of Mg-rich MgH2–TiH2 nanocomposites prepared by reactive ball milling under hydrogen gas, Phys. Chem. Chem. Phys. 14 (2012) 1200–1211. https://doi.org/10.1039/C1CP23030A.
[25] D. Aurbach, R. Turgeman, O. Chusid, Y. Gofer, Spectroelectrochemical studies of magnesium deposition by in situ FTIR spectroscopy, Electrochem. Commun. 3 (2001) 252–261. https://doi.org/10.1016/S1388-2481(01)00148-5.
[26] T. Liu, C. Chen, H. Wang, Y. Wu, Enhanced Hydrogen Storage Properties of Mg–Ti–V Nanocomposite at Moderate Temperatures, J. Phys. Chem. C. 118 (2014) 22419–22425. https://doi.org/10.1021/jp5061073.
[27] A. Zaluska, L. Zaluski, J. Ström–Olsen, Nanocrystalline magnesium for hydrogen storage, J. Alloys Compd. 288 (1999) 217–225. https://doi.org/10.1016/S0925-8388(99)00073-0.
[28] G. Barkhordarian, T. Klassen, R. Bormann, Effect of Nb2O5 content on hydrogen reaction kinetics of Mg, J. Alloys Compd. 364 (2004) 242–246. https://doi.org/10.1016/S0925-8388(03)00530-9.
[29] B.S. Amirkhiz, B. Zahiri, P. Kalisvaart, D. Mitlin, Synergy of elemental Fe and Ti promoting low temperature hydrogen sorption cycling of magnesium, Int. J. Hydrog. Energy. 36 (2011) 6711–6722. https://doi.org/10.1016/j.ijhydene.2011.02.141.
[30] A. Pan, T. Kar, A.K. Rakshit, S.P. Moulik, Enthalpy-Entropy Compensation (EEC) Effect: Decisive Role of Free Energy, J. Phys. Chem. B. 120 (2016) 10531–10539. https://doi.org/10.1021/acs.jpcb.6b05890.
[31] A. Pan, T. Biswas, A.K. Rakshit, S.P. Moulik, Enthalpy-Entropy Compensation (EEC) Effect: A Revisit, J. Phys. Chem. B. 119 (2015) 15876–15884. https://doi.org/10.1021/acs.jpcb.5b09925.
[32] N. Patelli, M. Calizzi, L. Pasquini, Interface Enthalpy-Entropy Competition in Nanoscale Metal Hydrides, Inorganics. 6 (2018) 13. https://doi.org/10.3390/inorganics6010013.
[33] V. Berube, G. Chen, M. Dresselhaus, Impact of nanostructuring on the enthalpy of formation of metal hydrides, Int. J. Hydrog. Energy. 33 (2008) 4122–4131. https://doi.org/10.1016/j.ijhydene.2008.05.083.
[34] C. Zlotea, Y. Oumellal, S.-J. Hwang, C.M. Ghimbeu, P.E. de Jongh, M. Latroche, Ultrasmall MgH2 Nanoparticles Embedded in an Ordered Microporous Carbon Exhibiting Rapid Hydrogen Sorption Kinetics, J. Phys. Chem. C. 119 (2015) 18091–18098. https://doi.org/10.1021/acs.jpcc.5b05754.
[35] M. Konarova, A. Tanksale, J. Norberto Beltramini, G. Qing Lu, Effects of nano-confinement on the hydrogen desorption properties of MgH2, Nano Energy. 2 (2013) 98–104. https://doi.org/10.1016/j.nanoen.2012.07.024.
[36] L.K. Wagner, E.H. Majzoub, M.D. Allendorf, J.C. Grossman, Tuning metal hydride thermodynamics via size and composition: Li-H, Mg-H, Al-H, and Mg-Al-H nanoclusters for hydrogen storage, Phys. Chem. Chem. Phys. 14 (2012) 6611–6616. https://doi.org/10.1039/c2cp24063g.
[37] J. Huang, J.F. Wan, C. Xie, J. Chen, C. Long, Structure analysis of surface layer on passivated magnesium powders, Mater. Lett. 61 (2007) 2430–2433. https://doi.org/10.1016/j.matlet.2006.09.029.
[38] J. Boulet, N. Gerard, The mechanism and kinetics of hydride formation in Mg-10wt.% Ni and CeMg12, J. Less-Common Met. 89 (1983) 151–161. https://doi.org/10.1016/0022-5088(83)90261-8.
[39] N. B. Arboleda Jr, H. Kasai, K. Nobuhara, W. A. Diño, H. Nakanishi, Dissociation and sticking of H2 on Mg (0001), Ti (0001) and La (0001) surfaces, J. Phys. Soc. Jpn. 73 (2004) 745–748. https://doi.org/10.1143/JPSJ.73.745.
[40] B. Hammer, J.K. Nørskov, Electronic factors determining the reactivity of metal surfaces, Surf. Sci. 343 (1995) 211–220. https://doi.org/10.1016/0039-6028(96)80007-0.
[41] M. Stioui, A. Grayevsky, A. Resnik, D. Shaltiel, N. Kaplan, Macroscopic and microscopic kinetics of hydrogen in magnesium-rich compounds, J. Less-Common Met. 123 (1986) 9–24. https://doi.org/10.1016/0022-5088(86)90110-4.
[42] J. Töpler, H. Buchner, H. Säufferer, K. Knorr, W. Prandl, Measurements of the diffusion of hydrogen atoms in magnesium and Mg2Ni by neutron scattering, J. Less-Common Met. 88 (1982) 397–404. https://doi.org/10.1016/0022-5088(82)90248-X.
[43] N.S. Norberg, T.S. Arthur, S.J. Fredrick, A.L. Prieto, Size-dependent hydrogen storage properties of Mg nanocrystals prepared from solution, J. Am. Chem. Soc. 133 (2011) 10679–10681. https://doi.org/10.1021/ja201791y.
[44] Y. Sun, C. Shen, Q. Lai, W. Liu, D.-W. Wang, K.-F. Aguey-Zinsou, Tailoring magnesium based materials for hydrogen storage through synthesis: Current state of the art, Energy Storage Mater. 10 (2018) 168–198. https://doi.org/10.1016/j.ensm.2017.01.010.
[45] R. Schulz, J. Huot, G. Liang, S. Boily, G. Lalande, M. Denis, J. Dodelet, Recent developments in the applications of nanocrystalline materials to hydrogen technologies, Mater. Sci. Eng: A. 267 (1999) 240–245. https://doi.org/10.1016/S0921-5093(99)00098-2.
[46] Y. Fu, L. Zhang, Y. Li, S. Guo, Z. Yu, W. Wang, K. Ren, Q. Peng, S. Han, Catalytic effect of MOF-derived transition metal catalyst FeCoS@ C on hydrogen storage of magnesium, J. Mater. Sci. Technol. 138 (2023) 59–69. https://doi.org/10.1016/j.jmst.2022.08.019.
[47] M. Felderhoff, B. Bogdanović, High temperature metal hydrides as heat storage materials for solar and related applications, Int. J. Mol. Sci. 10 (2009) 325–344. https://doi.org/10.3390/ijms10010325.
[48] P.E. de Jongh, P. Adelhelm, Nanosizing and nanoconfinement: new strategies towards meeting hydrogen storage goals, ChemSusChem. 3 (2010) 1332–1348. https://doi.org/10.1002/cssc.201000248.
[49] R.W. Wagemans, J.H. van Lenthe, P.E. de Jongh, A.J. van Dillen, K.P. de Jong, Hydrogen storage in magnesium clusters: quantum chemical study, J. Am. Chem. Soc. 127 (2005) 16675–16680. https://doi.org/10.1021/ja054569h.
[50] S. Krieck, H. Görls, M. Westerhausen, Mechanistic elucidation of the formation of the inverse Ca (I) sandwich complex [(thf) 3Ca (μ-C6H3-1, 3, 5-Ph3) Ca (thf) 3] and stability of aryl-substituted phenylcalcium complexes, J. Am. Chem. Soc. 132 (2010) 12492–12501. https://doi.org/10.1021/ja105534w.
[51] S.J. Bonyhady, D. Collis, G. Frenking, N. Holzmann, C. Jones, A. Stasch, Synthesis of a stable adduct of dialane(4) (Al2H4) via hydrogenation of a magnesium(I) dimer, Nat. Chem. 2 (2010) 865–869. https://doi.org/10.1038/nchem.762.
[52] J. Intemann, J. Spielmann, P. Sirsch, S. Harder, Well-defined molecular magnesium hydride clusters: relationship between size and hydrogen-elimination temperature, Chemistry. 19 (2013) 8478–8489. https://doi.org/10.1002/chem.201300684.
[53] A. Pan, B. Mandal, A.K. Rakshit, S.P. Moulik, A Rational Study of the Origin and Generality of Anti-Enthalpy–Entropy Compensation (AEEC) Phenomenon, Z. Phys. Chem. 232 (2018) 373–391. https://doi.org/10.1515/zpch-2017-1007.
[54] Y. Wang, Y. Wang, Recent advances in additive-enhanced magnesium hydride for hydrogen storage, Prog. Nat. Sci: Mater. Int. 27 (2017) 41–49. https://doi.org/10.1016/j.pnsc.2016.12.016.
[55] Q. Hou, X. Yang, J. Zhang, Review on hydrogen storage performance of MgH2: development and trends, ChemistrySelect. 6 (2021) 1589–1606. https://doi.org/10.1002/slct.202004476.
[56] W. Liu, K.-F. Aguey-Zinsou, Synthesis of highly dispersed nanosized LaNi5 on carbon: Revisiting particle size effects on hydrogen storage properties, Int. J. Hydrog. Energy. 41 (2016) 14429–14436. https://doi.org/10.1016/j.ijhydene.2016.02.024.
[57] E. Wiberg, H. Goeltzer, R. Bauer, Synthese von Magnesiumhydrid aus den Elementen, Z. Naturforsch. - B. 6 (1951) 394–395. https://doi.org/10.1515/znb-1951-0714.
[58] X. Wang, L. Andrews, Infrared spectra of magnesium hydride molecules, complexes, and solid magnesium dihydride, J. Phys. Chem. A. 108 (2004) 11511–11520. https://doi.org/10.1021/jp046410h.
[59] P. Vajeeston, P. Ravindran, A. Kjekshus, H. Fjellvag, Pressure-induced structural transitions in MgH2, Phys Rev Lett. 89 (2002) 175506. https://doi.org/10.1103/PhysRevLett.89.175506.
[60] D. Mukherjee, J. Okuda, Molecular Magnesium Hydrides, Angew. Chem. Int. Ed. Engl. 57 (2018) 1458–1473. https://doi.org/10.1002/anie.201708592.
[61] D. Gallagher, K. Henderson, A. Kennedy, C.T. O’ Hara, R.E. Mulvey, R.B. Rowlings, Chem. Commun. 2002 (2002) 376–377. http://dx.doi.org/10.1039/b110117j.
[62] H. Leng, Y. Pan, Q. Li, K.C. Chou, Effect of LiH on hydrogen storage property of MgH2, Int. J. Hydrog. Energy. 39 (2014) 13622–13627. https://doi.org/10.1016/j.ijhydene.2014.02.131.
[63] S.-I. Ri, K.-J. Um, J.-H. Wi, J.-C. Kim, N.-H. Kim, Effects of single– and co– substitution of Ti and Fe on vacancy formation and dehydrogenation from MgH2 (110) surface: Ab initio study, Int. J. Hydrog. Energy. 44 (2019) 22761–22769. https://doi.org/10.1016/j.ijhydene.2019.06.213.
[64] A. Borgschulte, U. Bösenberg, G. Barkhordarian, M. Dornheim, R. Bormann, Enhanced hydrogen sorption kinetics of magnesium by destabilized MgH2− δ, Catal. Today. 120 (2007) 262–269. https://doi.org/10.1016/j.cattod.2006.09.031.
[65] M.H. Mintz, Y. Zeiri, Hydriding kinetics of powders, J. Alloys Compd. 216 (1995) 159–175. https://doi.org/10.1016/0925-8388(94)01269-N.
[66] G. Barkhordarian, T. Klassen, R. Bormann, Kinetic investigation of the effect of milling time on the hydrogen sorption reaction of magnesium catalyzed with different Nb2O5 contents, J. Alloys Compd. 407 (2006) 249–255. https://doi.org/10.1016/j.jallcom.2005.05.037.
[67] E. Evard, I. Gabis, V. Yartys, Kinetics of hydrogen evolution from MgH2: experimental studies, mechanism and modelling, Int. J. Hydrog. Energy. 35 (2010) 9060–9069. https://doi.org/10.1016/j.ijhydene.2010.05.092.
[68] M. Tegel, S. Schöne, B. Kieback , L. Röntzsch, An efficient hydrolysis of MgH2-based materials, Int. J. Hydrog. Energy. 42 (2017) 2167–2176. https://doi.org/10.1016/j.ijhydene.2016.09.084.
[69] A. Bhatnagar, M.A. Shaz, O.N. Srivastava, Synthesis of MgH2 using autocatalytic effect of MgH2, Int. J. Hydrog. Energy. 44 (2019) 6738–6747. https://doi.org/10.1016/j.ijhydene.2019.01.163.
[70] H. Liu, P. Sun, R.C. Bowman, Z.Z. Fang, Y. Liu, C. Zhou, Effect of air exposure on hydrogen storage properties of catalyzed magnesium hydride, J. Power Sources. 454 (2020) 227936. https://doi.org/10.1016/j.jpowsour.2020.227936.
[71] M. Polanski, J. Bystrzycki, T. Plocinski, The effect of milling conditions on microstructure and hydrogen absorption/desorption properties of magnesium hydride (MgH2) without and with Cr2O3 nanoparticles, Int. J. Hydrog. Energy. 33 (2008) 1859–1867. https://doi.org/10.1016/j.ijhydene.2008.01.043.
[72] T. He, H. Cao, P. Chen, Complex Hydrides for Energy Storage, Conversion, and Utilization, Adv. Mater. 31 (2019) e1902757. https://doi.org/10.1002/adma.201902757.
[73] V.A. Yartys, M.V. Lototskyy, E. Akiba, R. Albert, V.E. Antonov, et al., Magnesium based materials for hydrogen based energy storage: Past, present and future, Int. J. Hydrog. Energy. 44 (2019) 7809–7859. https://doi.org/10.1016/j.ijhydene.2018.12.212.
[74] D. Elanski, J.-W. Lim, K. Mimura, M. Isshiki, Thermodynamic estimation of hydride formation during hydrogen plasma arc melting, J. Alloys Compd. 439 (2007) 210–214. https://doi.org/10.1016/j.jallcom.2006.04.076.
[75] J. Benjamin, T. Volin, The mechanism of mechanical alloying, Metall. Trans. 5 (1974) 1929–1934. https://doi.org/10.1007/bf02644161.
[76] C. Suryanarayana, Mechanical alloying and milling, Prog. Mater. Sci. 46 (2001) 1–184. https://doi.org/10.1016/S0079-6425(99)00010-9.
[77] S.-H. Hong, H.-J. Kim, M.Y. Song, Rate enhancement of hydrogen generation through the reaction of magnesium hydride with water by MgO addition and ball milling, J. Ind. Eng. Chem. 18 (2012) 405–408. https://doi.org/10.1016/j.jiec.2011.11.104.
[78] S.D. Vincent, J. Huot, Effect of air contamination on ball milling and cold rolling of magnesium hydride, J. Alloys Compd. 509 (2011) L175–L179. https://doi.org/10.1016/j.jallcom.2011.02.147.
[79] H.G. Schimmel, M.R. Johnson, G.J. Kearley, A.J. Ramirez-Cuesta, J. Huot, F.M. Mulder, Structural information on ball milled magnesium hydride from vibrational spectroscopy and ab-initio calculations, J. Alloys Compd. 393 (2005) 1–4. https://doi.org/10.1016/j.jallcom.2004.08.102.
[80] S. Dal Toè, S. Lo Russo, A. Maddalena, G. Principi, A. Saber, et al., Hydrogen desorption from magnesium hydride–graphite nanocomposites produced by ball milling, Mater. Sci. Eng: B. 108 (2004) 24–27. https://doi.org/10.1016/j.mseb.2003.10.030.
[81] J. Charbonnier, P. de Rango, D. Fruchart, S. Miraglia, L. Pontonnier, et al., Hydrogenation of transition element additives (Ti, V) during ball milling of magnesium hydride, J. Alloys Compd. 383 (2004) 205–208. https://doi.org/10.1016/j.jallcom.2004.04.059.
[82] W. Cao, Synthesis of nanomaterials by high energy ball milling, Skyspring Nanomaterials, Inc. (2007).
[83] H. Fecht, E. Hellstern, Z. Fu, W. Johnson, Nanocrystalline metals prepared by high-energy ball milling, Metall. Trans. A. 21 (1990) 2333–2337. https://doi.org/10.1007/BF02646980.
[84] R. Denys, A. Riabov, J. Maehlen, M. Lototsky, J. Solberg, V. Yartys, In situ synchrotron X-ray diffraction studies of hydrogen desorption and absorption properties of Mg and Mg–Mm–Ni after reactive ball milling in hydrogen, Acta Mater. 57 (2009) 3989–4000. https://doi.org/10.1016/j.actamat.2009.05.004.
[85] J. Huot, G. Liang, S. Boily, A. Van Neste, R. Schulz, Structural study and hydrogen sorption kinetics of ball-milled magnesium hydride, J. Alloys Compd. 293 (1999) 495–500. https://doi.org/10.1016/S0925-8388(99)00474-0.
[86] W.S. Tang, J.-N. Chotard, P. Raybaud, R. Janot, Enthalpy–Entropy Compensation Effect in Hydrogen Storage Materials: Striking Example of Alkali Silanides MSiH3 (M = K, Rb, Cs), J. Phys. Chem. C. 118 (2014) 3409–3419. https://doi.org/10.1021/jp411314w.
[87] W. Liu, K.-F. Aguey-Zinsou, Size effects and hydrogen storage properties of Mg nanoparticles synthesised by an electroless reduction method, J. Mater. Chem. A. 2 (2014) 9718–9726. https://doi.org/10.1039/c4ta01108b.
[88] N. Hanada, T. Ichikawa, S.-I. Orimo, H. Fujii, Correlation between hydrogen storage properties and structural characteristics in mechanically milled magnesium hydride MgH2, J. Alloys Compd. 366 (2004) 269–273. https://doi.org/10.1016/s0925-8388(03)00734-5.
[89] R.B.V. Campos, S.A.d.S. Camargo Junior, M.C. Brum, D.S.d. Santos, Hydrogen Uptake Enhancement by the Use of a Magnesium Hydride and Carbon Nanotubes Mixture, Mater. Res. 20 (2017) 85–88. https://doi.org/10.1590/1980-5373-mr-2017-0445.
[90] D.M. Mattox, Handbook of physical vapor deposition (PVD) processing, William Andrew. (2010). https://doi.org/10.1016/C2009-0-18800-1.
[91] Y. Xu, Y. Zhou, Y. Li, Y. Hao, P. Wu, Z. Ding, Recent advances in the preparation methods of magnesium-based hydrogen storage materials, Molecules. 29 (2024) 2451. https://doi.org/10.3390/molecules29112451.
[92] Y. Xu, Y. Li, Q. Hou, Y. Hao, Z. Ding, Ball milling innovations advance Mg-based hydrogen storage materials towards practical applications, Materials. 17 (2024) 2510. https://doi.org/10.3390/ma17112510.
[93] A. Soltani, F. Djani, D.E. Mazouzi, R.N.E. Tiri, A. Aygün, et al., ZnSnO3-SnO2 nanocomposite as a catalyst for efficient hydrogen production through sodium borohydride methanolysis, Int. J. Hydrog. Energy. 67 (2024) 429–437. https://doi.org/10.1016/j.ijhydene.2024.04.208.
[94] M. Song, L. Zhang, F. Wu, H. Zhang, H. Zhao, et al., Recent advances of magnesium hydride as an energy storage material, J. Mater. Sci. Technol. 149 (2023) 99–111. https://doi.org/10.1016/j.jmst.2022.11.032.
[95] D.A. Lanbaran, P.F. Kojour, C. Wang, C. Wen, Z. Wu, et al., Numerical investigation of pulsed heating effects on MgH2 desorption kinetics and thermal efficiency in solid-state hydrogen storage, Appl. Energy. 401 (2025) 126690. https://doi.org/10.1016/j.apenergy.2025.126690.
[96] J.C. Crivello, R.V. Denys, M. Dornheim, M. Felderhoff, D.M. Grant, et al., Mg-based compounds for hydrogen and energy storage, Appl. Phys. A. 122 (2016) 1–17. https://doi.org/10.1007/s00339-016-9601-1.
[97] U. Haussermann, H. Blomqvist, D. Noreus, Bonding and stability of the hydrogen storage material Mg(2)NiH(4), Inorg. Chem. 41 (2002) 3684–3692. https://doi.org/10.1021/ic0201046.
[98] P. Vajeeston, P. Ravindran, M. Fichtner, H. Fjellvag, Influence of crystal structure of bulk phase on the stability of nanoscale phases: investigation on MgH2 derived nanostructures, J. Phys. Chem. C. 116 (2012) 18965–18972. https://doi.org/10.1021/jp305933g.
[99] V. Berube, G. Radtke, M. Dresselhaus, G. Chen, Size effects on the hydrogen storage properties of nanostructured metal hydrides: A review, Int. J. Energy Res. 31 (2007) 637–663. https://doi.org/10.1002/er.1284.
[100] L. Berlouis, P. Honnor, P. Hall, S. Morris, S. Dodd, An investigation of the effect of Ti, Pd and Zr on the dehydriding kinetics of MgH2, J. Mater. Sci. 41 (2006) 6403–6408. https://doi.org/10.1007/s10853-006-0732-1.
[101] A. Kadri, Y. Jia, Z. Chen, X. Yao, Catalytically Enhanced Hydrogen Sorption in Mg-MgH2 by Coupling Vanadium-Based Catalyst and Carbon Nanotubes, Materials. 8 (2015) 3491–3507. https://doi.org/10.3390/ma8063491.
[102] J. Gulicovski, Ž. Rašković-Lovre, S. Kurko, R. Vujasin, Z. Jovanović, et al., Influence of vacant CeO2 nanostructured ceramics on MgH2 hydrogen desorption properties, Ceram. Int. 38 (2012) 1181–1186. https://doi.org/10.1016/j.ceramint.2011.08.047.
[103] S.D. Beattie, U. Setthanan, G.S. McGrady, Thermal desorption of hydrogen from magnesium hydride (MgH2): An in situ microscopy study by environmental SEM and TEM, Int. J. Hydrog. Energy. 36 (2011) 6014–6021. https://doi.org/10.1016/j.ijhydene.2011.02.026.
[104] Y.-h. Zhang, Z.-c. Liu, B.-w. Li, Z.-h. Ma, S.-h. Guo, X.-l. Wang, Structure and electrochemical performances of Mg2Ni1− xMnx (x= 0–0.4) electrode alloys prepared by melt spinning, Electrochim. Acta. 56 (2010) 427–434. https://doi.org/10.1016/j.electacta.2010.08.058.
[105] Y.S. Au, M. Ponthieu, R. van Zwienen, C. Zlotea, F. Cuevas, et al., Synthesis of Mg 2 Cu nanoparticles on carbon supports with enhanced hydrogen sorption kinetics, J. Mater. Chem. A. 1 (2013) 9983–9991. https://doi.org/10.1039/C3TA10926G.
[106] M. Danaie, D. Mitlin, TEM analysis and sorption properties of high-energy milled MgH2 powders, J. Alloys Compd. 476 (2009) 590–598. https://doi.org/10.1016/j.jallcom.2008.09.078.
[107] C. Shang, Z. Guo, Effect of carbon on hydrogen desorption and absorption of mechanically milled MgH2, J. Power Sources. 129 (2004) 73–80. https://doi.org/10.1016/j.jpowsour.2003.11.013.
[108] N. Hanada, T. Ichikawa, H. Fujii, Catalytic effect of Ni nano-particle and Nb oxide on H-desorption properties in MgH2 prepared by ball milling, J. Alloys Compd. 404 (2005) 716–719. https://doi.org/10.1016/j.jallcom.2004.12.166.
[109] H. Simchi, A. Kaflou, A. Simchi, Synergetic effect of Ni and Nb2O5 on dehydrogenation properties of nanostructured MgH2 synthesized by high-energy mechanical alloying, Int. J. Hydrog. Energy. 34 (2009) 7724–7730. https://doi.org/10.1016/j.ijhydene.2009.07.038.
[110] V. Fuster, G. Urretavizcaya, F. Castro, Characterization of MgH2 formation by low-energy ball-milling of Mg and Mg+ C (graphite) mixtures under H2 atmosphere, J. Alloys Compd. 481 (2009) 673–680. https://doi.org/10.1016/j.jallcom.2009.03.056.
[111] P.-A. Huhn, M. Dornheim, T. Klassen, R. Bormann, Thermal stability of nanocrystalline magnesium for hydrogen storage, J. Alloys Compd. 404 (2005) 499–502. https://doi.org/10.1016/j.jallcom.2004.10.087.
[112] O. Friedrichs, F. Aguey-Zinsou, J.A. Fernandez, J. Sanchez-Lopez, A. Justo, et al., MgH2 with Nb2O5 as additive, for hydrogen storage: Chemical, structural and kinetic behavior with heating, Acta Mater. 54 (2006) 105–110. https://doi.org/10.1016/j.actamat.2005.08.024.
[113] M. Polanski, J. Bystrzycki, Comparative studies of the influence of different nano-sized metal oxides on the hydrogen sorption properties of magnesium hydride, J. Alloys Compd. 486 (2009) 697–701. https://doi.org/10.1016/j.jallcom.2009.07.042.
[114] M. Verón, H. Troiani, F. Gennari, Synergetic effect of Co and carbon nanotubes on MgH2 sorption properties, Carbon. 49 (2011) 2413–2423. https://doi.org/10.1016/j.carbon.2011.02.008.
[115] A. Ranjbar, Z. Guo, X. Yu, D. Attard, A. Calka, H.-K. Liu, Effects of SiC nanoparticles with and without Ni on the hydrogen storage properties of MgH2, Int. J. Hydrog. Energy. 34 (2009) 7263–7268. https://doi.org/10.1016/j.ijhydene.2009.07.005.
[116] S.-A. Jin, J.-H. Shim, Y.W. Cho, K.-W. Yi, Dehydrogenation and hydrogenation characteristics of MgH2 with transition metal fluorides, J. Power Sources. 172 (2007) 859–862. https://doi.org/10.1016/j.jpowsour.2007.04.090.
[117] T. Czujko, Z. Zaranski, I. Malka, Z. Wronski, Composite behaviour of MgH2 and complex hydride mixtures synthesized by ball milling, J. Alloys Compd. 509 (2011) S604–S607. https://doi.org/10.1016/j.jallcom.2010.08.133.
[118] C. Wu, P. Wang, X. Yao, C. Liu, D. Chen, G. Lu, H. Cheng, Effect of carbon/noncarbon addition on hydrogen storage behaviors of magnesium hydride, J. Alloys Compd. 414 (2006) 259–264. https://doi.org/10.1016/j.jallcom.2005.07.021.
[119] H. Gasan, O.N. Celik, N. Aydinbeyli, Y.M. Yaman, Effect of V, Nb, Ti and graphite additions on the hydrogen desorption temperature of magnesium hydride, Int. J. Hydrog. Energy. 37 (2012) 1912–1918. https://doi.org/10.1016/j.ijhydene.2011.05.086.
[120] C.J. Webb, A review of catalyst-enhanced magnesium hydride as a hydrogen storage material, J. Phys. Chem. Solids. 84 (2015) 96–106. https://doi.org/10.1016/j.jpcs.2014.06.014.
[121] R. Gremaud, C.P. Broedersz, D.M. Borsa, A. Borgschulte, P. Mauron, et al., Hydrogenography: an optical combinatorial method to find new light‐weight hydrogen‐storage materials, Adv. Mater. 19 (2007) 2813–2817. https://doi.org/10.1002/adma.200602560.
[122] G. Cao, Nanostructures & nanomaterials: synthesis, properties & applications, Imperial College Press. (2004). https://doi.org/10.1021/ja0409457.
[123] L. Garcia, C. Dinoi, M.F. Mahon, L. Maron, M.S. Hill, Magnesium hydride alkene insertion and catalytic hydrosilylation, Chem. Sci. 10 (2019) 8108–8118. https://doi.org/10.1039/c9sc02056j.
[124] M. Martin, C. Gommel, C. Borkhart, E. Fromm, Absorption and desorption kinetics of hydrogen storage alloys, J. Alloys Compd. 238 (1996) 193–201. https://doi.org/10.1016/0925-8388(96)02217-7.
[125] A. Khawam, D.R. Flanagan, Solid-state kinetic models: basics and mathematical fundamentals, J. Phys. Chem. B. 110 (2006) 17315–17328. https://doi.org/10.1021/jp062746a.
[126] M. Pozzo, D. Alfe, Hydrogen dissociation and diffusion on transition metal (= Ti, Zr, V, Fe, Ru, Co, Rh, Ni, Pd, Cu, Ag)-doped Mg (0001) surfaces, Int. J. Hydrog. Energy. 34 (2009) 1922–1930. https://doi.org/10.1016/j.ijhydene.2008.11.109.
[127] M. Pozzo, D. Alfe, A. Amieiro, S. French, A. Pratt, Hydrogen dissociation and diffusion on Ni- and Ti-doped Mg(0001) surfaces, J. Chem. Phys. 128 (2008) 094703. https://doi.org/10.1063/1.2835541.
[128] P. Spatz, H. Aebischer, A. Krozer, L. Schlapbach, The diffusion of H in Mg and the nucleation and growth of MgH2 in thin films, Z. Phys. Chem. 181 (1993) 393–397. https://doi.org/10.1524/zpch.1993.181.Part_1_2.393.
[129] M. Zhu, Y. Lu, L. Ouyang, H. Wang, Thermodynamic Tuning of Mg-Based Hydrogen Storage Alloys: A Review, Materials (Basel). 6 (2013) 4654–4674. https://doi.org/10.3390/ma6104654.
[130] H. Wang, H.J. Lin, W.T. Cai, L.Z. Ouyang, M. Zhu, Tuning kinetics and thermodynamics of hydrogen storage in light metal element based systems – A review of recent progress, J. Alloys Compd. 658 (2016) 280–300. https://doi.org/10.1016/j.jallcom.2015.10.090.
[131] H. Lin, L. Ouyang, H. Wang, D. Zhao, W. Wang, et al., Hydrogen storage properties of Mg–Ce–Ni nanocomposite induced from amorphous precursor with the highest Mg content, Int. J. Hydrog. Energy. 37 (2012) 14329–14335. https://doi.org/10.1016/j.ijhydene.2012.07.073.
[132] L. Ouyang, F. Qin, M. Zhu, The hydrogen storage behavior of Mg3La and Mg3LaNi0.1, Scr. Mater. 55 (2006) 1075–1078. https://doi.org/10.1016/j.scriptamat.2006.08.052.
[133] V. Skripnyuk, E. Rabkin, Mg3Cd: A model alloy for studying the destabilization of magnesium hydride, Int. J. Hydrog. Energy. 37 (2012) 10724–10732. https://doi.org/10.1016/j.ijhydene.2012.04.065.
[134] T.Z. Si, J.B. Zhang, D.M. Liu, Q.A. Zhang, A new reversible Mg3Ag–H2 system for hydrogen storage, J. Alloys Compd. 581 (2013) 246–249. https://doi.org/10.1016/j.jallcom.2013.07.054.
[135] A. Asselli, J. Huot, Investigation of Effect of Milling Atmosphere and Starting Composition on Mg2FeH6 Formation, Metals. 4 (2014) 388–400. https://doi.org/10.3390/met4030388.
[136] X. Xiao, C. Xu, J. Shao, L. Zhang, T. Qin, et al., Remarkable hydrogen desorption properties and mechanisms of the Mg2FeH6@MgH2core–shell nanostructure, J. Mater. Chem. A. 3 (2015) 5517–5524. https://doi.org/10.1039/c4ta06837h.
[137] S. Garrier, B. Delhomme, P. De Rango, P. Marty, D. Fruchart, S. Miraglia, A new MgH2 tank concept using a phase-change material to store the heat of reaction, Int. J. Hydrog. Energy. 38 (2013) 9766–9771. https://doi.org/10.1016/j.ijhydene.2013.05.026.
[138] S. Vincent, J. Lang, J. Huot, Addition of catalysts to magnesium hydride by means of cold rolling, J. Alloys Compd. 512 (2012) 290–295. https://doi.org/10.1016/j.jallcom.2011.09.084.
[139] L.-P. Ma, P. Wang, X.-D. Kang, H.-M. Cheng, Preliminary investigation on the catalytic mechanism of TiF3 additive in MgH2–TiF3H-storage system, J. Mater. Res. 22 (2007) 1779–1786. https://doi.org/10.1557/jmr.2007.0239.
[140] C. Zhou, Z.Z. Fang, C. Ren, J. Li, J. Lu, Effect of Ti Intermetallic Catalysts on Hydrogen Storage Properties of Magnesium Hydride, J. Phys. Chem. C. 117 (2013) 12973–12980. https://doi.org/10.1021/jp402770p.
[141] C. Lu, J. Zou, X. Shi, X. Zeng, W. Ding, Synthesis and hydrogen storage properties of core–shell structured binary Mg@Ti and ternary Mg@Ti@Ni composites, Int. J. Hydrog. Energy. 42 (2017) 2239–2247. https://doi.org/10.1016/j.ijhydene.2016.10.088.
[142] D. Croston, D. Grant, G. Walker, The catalytic effect of titanium oxide based additives on the dehydrogenation and hydrogenation of milled MgH2, J. Alloys Compd. 492 (2010) 251–258. https://doi.org/10.1016/j.jallcom.2009.10.199.
[143] J. Cui, H. Wang, J. Liu, L. Ouyang, Q. Zhang, et al., Remarkable enhancement in dehydrogenation of MgH2 by a nano-coating of multi-valence Ti-based catalysts, J. Mater. Chem. A. 1 (2013) 5603–5611. https://doi.org/10.1039/C3TA01332D.
[144] J. Lu, Y.J. Choi, Z.Z. Fang, H.Y. Sohn, E. Ronnebro, Hydrogenation of nanocrystalline Mg at room temperature in the presence of TiH2, J. Am. Chem. Soc. 132 (2010) 6616–6617. https://doi.org/10.1021/ja910944w.
[145] W. Oelerich, T. Klassen, R. Bormann, Mg-based hydrogen storage materials with improved hydrogen sorption, Mater. Transact. 42 (2001) 1588–1592. https://doi.org/10.2320/matertrans.42.1588.
[146] P. Wang, A. Wang, H. Zhang, B. Ding, Z. Hu, Hydrogenation characteristics of Mg–TiO2 (rutile) composite, J. Alloys Compd. 313 (2000) 218–223. https://doi.org/10.1016/S0925-8388(00)01188-9.
[147] W. Kalisvaart, C. Harrower, J. Haagsma, B. Zahiri, E. Luber, et al., Hydrogen storage in binary and ternary Mg-based alloys: A comprehensive experimental study, Int. J. Hydrog. Energy. 35 (2010) 2091–2103. https://doi.org/10.1016/j.ijhydene.2009.12.013.
[148] X. Yao, C. Wu, A. Du, J. Zou, Z. Zhu, et al., Metallic and carbon nanotube-catalyzed coupling of hydrogenation in magnesium, J. Am. Chem. Soc. 129 (2007) 15650–15654. https://doi.org/10.1021/ja0751431.
[149] B. Vigeholm, J. Kjøller, B. Larsen, A.S. Pedersen, Formation and decomposition of magnesium hydride, J. Less-Common Met. 89 (1983) 135–144. https://doi.org/10.1016/0022-5088(83)90259-X.
[150] A. Kucharczyk, K. Naplocha, J.W. Kaczmar, H. Dieringa, K.U. Kainer, Current Status and Recent Developments in Porous Magnesium Fabrication, Adv. Eng. Mater. 20 (2017) 1700562. https://doi.org/10.1002/adem.201700562.
[151] D.-H. Yang, B.-Y. Hur, S.-R. Yang, Study on fabrication and foaming mechanism of Mg foam using CaCO3 as blowing agent, J. Alloys Compd. 461 (2008) 221–227. https://doi.org/10.1016/j.jallcom.2007.07.098.
[152] P. Li, N.V. Nguyen, H. Hao, Dynamic compressive behaviour of Mg foams manufactured by the direct foaming process, Mater. Design. 89 (2016) 636–641. https://doi.org/10.1016/j.matdes.2015.10.021.
[153] N.T. Kirkland, I. Kolbeinsson, T. Woodfield, G. Dias, M.P. Staiger, Processing-property relationships of as-cast magnesium foams with controllable architecture, Int. J. Mod. Phys. B. 23 (2009) 1002–1008. https://doi.org/10.1142/S0217979209060373.
[154] A. Jinnapat, A. Kennedy, The manufacture of spherical salt beads and their use as dissolvable templates for the production of cellular solids via a powder metallurgy route, J. Alloys Compd. 499 (2010) 43–47. https://doi.org/10.1016/j.jallcom.2010.03.132.
[155] F. Witte, H. Ulrich, M. Rudert, E. Willbold, Biodegradable magnesium scaffolds: Part 1: appropriate inflammatory response, J. Biomed. Mater. Res. A. 81 (2007) 748–756. https://doi.org/10.1002/jbm.a.31170.
[156] J. Capek, D. Vojtech, Properties of porous magnesium prepared by powder metallurgy, Mater. Sci. Eng. C. Mater. Biol. Appl. 33 (2013) 564–569. https://doi.org/10.1016/j.msec.2012.10.002.
[157] Z.-k. Xie, M. Tane, S.-k. Hyun, Y. Okuda, H. Nakajima, Vibration–damping capacity of lotus-type porous magnesium, Mater. Sci. Eng: A. 417 (2006) 129–133. https://doi.org/10.1016/j.msea.2005.10.061.
[158] A.H. Yusop, A.A. Bakir, N.A. Shaharom, M.R. Abdul Kadir, H. Hermawan, Porous biodegradable metals for hard tissue scaffolds: a review, Int. J. Biomater. 2012 (2012) 641430. https://doi.org/10.1155/2012/641430.
[159] Y. Bi, Y. Zheng, Y. Li, Microstructure and mechanical properties of sintered porous magnesium using polymethyl methacrylate as the space holder, Mater. Lett. 161 (2015) 583–586. https://doi.org/10.1016/j.matlet.2015.09.039.
[160] X. Wang, Z. Li, Y. Huang, K. Wang, X. Wang, F. Han, Processing of magnesium foams by weakly corrosive and highly flexible space holder materials, Mater. Design. 64 (2014) 324–329. https://doi.org/10.1016/j.matdes.2014.07.049.
[161] C. Zhou, Z.Z. Fang, J. Lu, X. Zhang, Thermodynamic and kinetic destabilization of magnesium hydride using Mg-In solid solution alloys, J. Am. Chem. Soc. 135 (2013) 10982–10985. https://doi.org/10.1021/ja4058794.
[162] S. Agarwal, A. Aurora, A. Jain, I. Jain, A. Montone, Catalytic effect of ZrCrNi alloy on hydriding properties of MgH2, Int. J. Hydrog. Energy. 34 (2009) 9157–9162. https://doi.org/10.1016/j.ijhydene.2009.09.034.
[163] S. Brutti, G. Mulas, E. Piciollo, S. Panero, P. Reale, Magnesium hydride as a high capacity negative electrode for lithium ion batteries, J. Mater. Chem. 22 (2012) 14531–14537. https://doi.org/10.1039/c2jm31827j.
[164] A. Chaise, P. de Rango, P. Marty, D. Fruchart, Experimental and numerical study of a magnesium hydride tank, Int. J. Hydrog. Energy. 35 (2010) 6311–6322. https://doi.org/10.1016/j.ijhydene.2010.03.057.
[165] V. Berube, M. Dresselhaus, G. Chen, Entropy stabilization of deformed regions characterized by an excess volume for hydrogen storage applications, Int. J. Hydrog. Energy. 34 (2009) 1862–1872. https://doi.org/10.1016/j.ijhydene.2008.11.096.
Cited By
Submitted
2025-07-16
Available online
2025-09-30
How to Cite
Borchloo, A., & Nekouee, K. (2025). A review of enhanced hydrogen storage in MgH2: the role of high-energy reactive ball milling and catalysis. Synthesis and Sintering, 5(3), 200-230. https://doi.org/10.53063/synsint.2025.53296
Issue
Copyright (c) 2025 Ali Borchloo, Khanali Nekouee
This work is licensed under a Creative Commons Attribution 4.0 International License.
Copyright
Authors are the copyright holders of their published papers in Synthesis and Sintering, which are simultaneously licensed under a Creative Commons Attribution 4.0 International License. The full details of the license are available at https://creativecommons.org/licenses/by/4.0/.
All papers published open access will be immediately and permanently free for everyone to read, download, copy, distribute, print, search, link to the full-text of papers, crawl them for indexing, pass them as data to software, or use them for any other lawful purpose without any registration obstacles or subscription fees.