Enhancing the antibacterial properties of zinc sulfide thin films by substrate patterning en en To investigate the porosity and substrate effects on the antibacterial properties of ZnS thin films, sculptured structures were considered. Two types of uncoated glass and primary coated glass were used as different substrates. Since the porosity percentage is dependent on the shadow of grains, spiral structures with different numbers of pitches were formed on the different substrates. The cross-section and morphology of the samples were investigated by means of FESEM images. To evaluate the antibacterial properties of the samples under light irradiation, the absorption spectra of the structures at different wavelengths were obtained and investigated. The results showed that most adsorption of structures occurs at wavelengths less than 400 nm. Finally, antibacterial properties of this thin film were investigated in two cases of without light and with light irradiation, for two types of Escherichia coli and Staphylococcus aureus bacteria. The results showed that the structures with higher porosity have better antibacterial properties. The results also showed that light radiation increases the antibacterial properties of structures. 191 199 Fatemeh Abdi Department of Engineering Sciences, Faculty of Advanced Technologies University of Mohaghegh Ardabili, Namin Iran F.Abdi@uma.ac.ir Solmaz Kia Department of Engineering Sciences, Faculty of Advanced Technologies University of Mohaghegh Ardabili, Namin Iran Sculptured thin films Spiral Antibacterial property Ultraviolet light Zinc sulfide Vol 5 No 3 Paper 3.pdf [1] W.C. Chan, D.J. Maxwell, X. Gao, R.E. Bailey, M. Han, S. Nie, Luminescent quantum dots for multiplexed biological detection and imaging, Curr. Opin. Biotechnol. 13 (2002) 40–46. https://doi.org/10.1016/S0958-1669(02)00282-3. ##[2] L. Coultas, K. Chawengsaksophak, J. Rossant, Endothelial cells and VEGF in vascular development, Nature. 438 (2005) 937–945. https://doi.org/10.1038/nature04479. ##[3] W.C. Chan, S. Nie, Quantum dot bioconjugates for ultrasensitive nonisotopic detection, Science. 281 (1998) 2016–2018. https://doi.org/10.1126/science.281.5385.2016. ##[4] G.R. Amiri, M.H. Yousefi, M.R. Aboulhassani, M.H. Keshavarz, D. Shahbazi, et al., Radar absorption of Ni0.7Zn0.3Fe2O4 nanoparticles, Digest J. Nanomater. Biostruct. 5 (2010) 719–725. ##[5] W.H. Yang, G.C. Schatz, R.P. Duyne, Discrete dipole approximation for calculating extinction and Raman intensities for small particles with arbitrary shapes, J. Chem. Phys. 103 (1995) 869–875. https://doi.org/10.1063/1.469787. ##[6] H. Katayama, S. Oda, H. Kukimoto, ZnS blue‐light‐emitting diodes with an external quantum efficiency of 5× 10−4, Appl. Phys. Lett. 27 (1975) 697–699. https://doi.org/10.1063/1.88350. ##[7] N. Fathy, R. Kobayashi, M. Ichimura, Preparation of ZnS thin films by the pulsed electrochemical deposition, Mater. Sci. Eng: B. 107 (2004) 271–276. https://doi.org/10.1016/j.mseb.2003.11.021. ##[8] A. Ates, M.A. Yıldırım, M. Kundakcı, A. Astam, Annealing and light effect on optical and electrical properties of ZnS thin films grown with the Silar method, Mater. Sci. Semicond. Process. 10 (2007) 281–286. https://doi.org/10.1016/j.mssp.2008.04.003. ##[9] D. Lincot, R.O. Borges, Chemical bath deposition of cadmium sulfide thin films. In situ growth and structural studies by combined quartz crystal microbalance and electrochemical impedance techniques, J. Electrochem. Soc. 139 (1992) 1880. https://doi.org/10.1149/1.2069515. ##[10] T.V. Prevenslik, Acoustoluminescence and sonoluminescence, J. Lumin. 87 (2000) 1210–1212. https://doi.org/10.1016/S0022-2313(99)00513-X. ##[11] D. Chen, F. Huang, G. Ren, D. Li, M. Zheng, et al., ZnS nano-architectures: photocatalysis, deactivation and regeneration, Nanoscale. 2 (2010) 2062–2064. https://doi.org/10.1039/C0NR00171F. ##[12] S. Yanagida, K. Mizumoto, C. Pac, Semiconductor photocatalysis. Part 6. Cis-trans photoisomerization of simple alkenes induced by trapped holes at surface states, J. Am. Chem. Soc. 108 (1986) 647–654. https://doi.org/10.1021/ja00264a014. ##[13] J.S. Hu, L.L. Ren, Y.G. Guo, H.P. Liang, A.M. Cao, et al., Mass production and high photocatalytic activity of ZnS nanoporous nanoparticles, Angew. Chem. 117 (2005) 1295–1299. https://doi.org/10.1002/anie.200462057. ##[14] H. Fujiwara, K. Murakoshi, Y. Wada, S. Yanagida, Observation of adsorbed N, N-dimethylformamide molecules on colloidal ZnS nanocrystallites, Effect of coexistent counteranion on surface structure, Langmuir. 14 (1998) 4070–4073. https://doi.org/10.1021/la9712855. ##[15] M.P. Valkonen, S. Lindroos, T. Kanniainen, M. Leskelä, U. Tapper, E. Kauppinen, Thin multilayer CdS/ZnS films grown by Silar technique, Appl. Surf. Sci. 120 (1997) 58–64. https://doi.org/10.1016/S0169-4332(97)00248-1. ##[16] Y.F. Nicolau, J.C. Menard, Solution growth of ZnS, CdS and Zn1-xCdxS thin films by the successive ionic-layer adsorption and reaction process; growth mechanism, J. Cryst. growth. 92 (1988) 128–142. https://doi.org/10.1016/0022-0248(88)90443-5. ##[17] H. Murray, A. Tosser, Photoconduction et effets photovoltaïques dans des couches minces pulverisées de ZnS, Thin Solid Films. 24 (1974) 165–180. https://doi.org/10.1016/0040-6090(74)90262-4. ##[18] H.L. Kwok, A study of ultra-thin CuxS-CdyZn1-yS polycrystalline solar cells, J. Phys. D: Appl. Phys. 16 (1983) 2367. https://doi.org/10.1088/0022-3727/16/12/015. ##[19] O.M. Hussain, P.S. Reddy, B.S. Naidu, S. Uthanna, P.J. Reddy, Characterization of thin film ZnCdS/CdTe solar cell, Semicond. Sci. Technol. 6 (1991) 690. https://doi.org/10.1088/0268-1242/6/7/023. ##[20] J.M. Doña, J. Herrero, Process and film characterization of chemical‐bath‐deposited ZnS thin films, J. Electrochem. Soc. 141 (1994) 205. https://doi.org/10.1149/1.2054685. ##[21] F. Rahman, M. Zahan, J. Podder, Synthesis of nanocrystalline ZnS thin films via spray pyrolysis for optoelectronic devices, Sens. Transduc. 149 (2013) 54–59. ##[22] J. Lee, S. Lee, S. Cho, S. Kim, L.Y. Park, Y.D. Choi, Role of growth parameters on structural and optical properties of ZnS nanocluster thin films grown by solution growth technique, Mater. Chem. Phys. 77 (2003) 254–260. https://doi.org/10.1016/S0254-0584(01)00563-6. ##[23] I. Dékány, L. Nagy, L.Turi, Z. Király, N.A. Kotov, J.H. Fendler, Preparation and characterization of CdS and ZnS particles in nanophase reactors provided by binary liquids adsorbed at colloidal silica particles, Langmuir. 12 (1996) 3709–3715. https://doi.org/10.1021/la951541i. ##[24] P.K. Ghosh, S. Jana, S. Nandy, K.K. Chattopadhyay, Size-dependent optical and dielectric properties of nanocrystalline ZnS thin films synthesized via rf-magnetron sputtering technique, Mater. Res. Bull. 42 (2007) 505–514. https://doi.org/10.1016/j.materresbull.2006.06.019. ##[25] M.Y. Nadeem, W. Ahmed, Optical properties of ZnS thin films, Turk. J. Phys. 24 (2000) 651–659. ##[26] H.J. Lee, S.I. Lee, Deposition and optical properties of nanocrystalline ZnS thin films by a chemical method, Curr. Appl. Phys. 7 (2007) 193–197. https://doi.org/10.1016/j.cap.2006.03.005. ##[27] T. Asahi, H. Yamashita, T. Maekawa, Preparation and optical properties of ZnS-microcrystals deposited in silica gels, Ceram. Int. 27 (2001) 39–43. https://doi.org/10.1016/S0272-8842(00)00039-0. ##[28] N. Fathy, M. Ichimura, Photoelectrical properties of ZnS thin films deposited from aqueous solution using pulsed electrochemical deposition, Sol. Energy Mater. 87 (2005) 747–756. https://doi.org/10.1016/j.solmat.2004.07.048. ##[29] M.A. Yildirim, A. Ateş, A. Astam, Annealing and light effect on structural, optical and electrical properties of CuS, CuZnS and ZnS thin films grown by the silar method, Phys. E: Low-dimens. Sys. Nanostruct. 41 (2009) 1365–1372. https://doi.org/10.1016/j.physe.2009.04.014. ##[30] H.K. Sadekar, N.G. Deshpande, Y.G. Gudage, A. Ghosh, S.D. Chavhan, et al., Growth, structural, optical and electrical study of ZnS thin films deposited by solution growth technique (SGT), J. Alloys Compd. 453 (2008) 519–524. https://doi.org/10.1016/j.jallcom.2007.10.123. ##[31] B. Elidrissi, M. Addou, M. Regragui, A. Bougrine, A. Kachouane, J.C. Bernede, Structure, composition and optical properties of ZnS thin films prepared by spray pyrolysis, Mater. Chem. Phys. 68 (2001) 175–179. https://doi.org/10.1016/S0254-0584(00)00351-5. ##[32] H.F. Zhang, C.M. Wang, E.C. Buck, L.S. Wang, Synthesis, characterization, and manipulation of helical SiO2 nanosprings, Nano Lett. 3 (2003) 577–580. https://doi.org/10.1021/nl0341180. ##[33] F. Wang, A. Lakhtakia, Response of slanted chiral sculptured thin films to dipolar sources, Opt. Commun. 235 (2004) 133–151. https://doi.org/10.1016/j.optcom.2004.03.016. ##[34] F. Wang, A. Lakhtakia, Lateral shifts of optical beams on reflection by slanted chiral sculptured thin films, Opt. Commun. 235 (2004) 107–132. https://doi.org/10.1016/j.optcom.2004.02.050. ##[35] J.M. Nieuwenhuizen, H.B. Haanstra, Microfractography of thin films, Philips Tech. Rev. 27 (1966) 87–91. ##[36] R. Messier, J.E. Yehoda, Geometry of thin‐film morphology, J. Appl. Phys. 58 (1985) 3739–3746. https://doi.org/10.1063/1.335639. ##[37] T. Motohiro,Y. Taga, Thin film retardation plate by oblique deposition, Appl. Opt. 28 (1989) 2466–2482. https://doi.org/10.1364/AO.28.002466. ##[38] K. Robbie, M.J. Brett, Sculptured thin films and glancing angle deposition: Growth mechanics and applications, J. Vac. Sci. Technol. A: Vac. Surf. Films. 15 (1997) 1460–1465. https://doi.org/10.1116/1.580562. ##[39] S.R. Kennedy, M.J. Brett, O. Toader, S. John, Fabrication of tetragonal square spiral photonic crystals, Nano Lett. 2 (2002) 59–62. https://doi.org/10.1021/nl015635q. ##[40] W. Daranfed, M.S. Aida, A. Hafdallah, H. Lekiket, Substrate temperature influence on ZnS thin films prepared by ultrasonic spray, Thin Solid Films. 518 (2009) 1082–1084. https://doi.org/10.1016/j.tsf.2009.03.227. ##[41] P.K. Bowen, J. Drelich, J. Goldman, Zinc exhibits ideal physiological corrosion behavior for bioabsorbable stents, Adv. Mater. 25 (2013) 2577–2582. https://doi.org/10.1002/adma.201300226. ##[42] D. Vojtěch, J. Kubásek, J. Šerák, P. Novák, Mechanical and corrosion properties of newly developed biodegradable Zn-based alloys for bone fixation, Acta Biomater. 7 (2011) 3515–3522. https://doi.org/10.1016/j.actbio.2011.05.008. ##[43] A.D. Campo, C. Echeverría, M.S. Martín, R.C. Rodríguez, M.F. García, A.M. Bonilla, Porous Microstructured Surfaces with pH‐Triggered Antibacterial Properties, Macromol. Biosci. 19 (2019) 1900127. https://doi.org/10.1002/mabi.201900127. ##[44] Z. Morshedtalab, G. Rahimi, A. Emami-Nejad, A. Farasat, A. Mohammadbeygi, et al., Antibacterial assessment of zinc sulfide nanoparticles against Streptococcus pyogenes and Acinetobacter baumannii, Curr. Top. Med. Chem. 20 (2020) 1042–1055. https://doi.org/10.2174/1381612826666200406095246. ##[45] G.R. Amir, S. Fatahian, N. Kianpour, Investigation of ZnS nanoparticle antibacterial effect, Curr. Nanosci. 10 (2014) 796–800. https://doi.org/10.2174/1573413710666140604220007. ##[46] S.K. Mani, M. Saroja, M. Venkatachalam, T. Rajamanickam, Antimicrobial activity and photocatalytic degradation properties of zinc sulfide nanoparticles synthesized by using plant extracts, J. Nanostruct. 8 (2018) 107–118. https://doi.org/10.22052/JNS.2018.02.001. ##[47] F.W. Aldbea, Z. Abdoorhman, R.A. Almahdi, M. Kraini, N.A. Imrigha, Structural Properties and Antibacterial Activity of Zinc Sulfide Nanoparticles, NanoWorld J. 9 (2023) 127–132. https://doi.org/10.17756/nwj.2023-124. ##[48] K.R. Raghupathi, R.T. Koodali, A.C. Manna, Size-dependent bacterial growth inhibition and mechanism of antibacterial activity of zinc oxide nanoparticles, Langmuir. 27 (2011) 4020–4028. https://doi.org/10.1021/la104825u. ##[49] F. Long, W.M. Wang, Z.K. Cui, L.Z. Fan, Z.G. Zou, T.K. Jia, An improved method for chemical bath deposition of ZnS thin films, Chem. Phys. Lett. 462 (2008) 84–87. https://doi.org/10.1016/j.cplett.2008.07.064. ##[50] F. Abdi, S. Kia, Designing and fabrication of zinc sulfide helical shape sculptured thin films and study of antibacterial properties of these porous structures, Metall. Eng. 24 (2021) 42–49. https://doi.org/10.22076/me.2022.527132.1312.